Mixing environment: temperature is 23±1℃, relative humidity is 50±5%; recommended powder-liquid ratio: 1.6g:0.5ml.
When mixing, first divide the weighed powder into three piles of large, medium and small and place them on a clean and sterilized glass plate, and then transfer the three piles of small, medium and large powder into the corresponding liquid and mix thoroughly before use. The blending time is no more than 90 seconds.
Complete the operation within 3-10 minutes after the net curing time of the product, and after curing for 24 hours, the compressive strength is ≥25MPa.
Immediately after use, remove excess material with a damp cotton ball or other instrument.
The water dissolution rate of the cement is not more than 1.5%.
The acid-soluble arsenic content of the cement does not exceed 2 mg/kg.
The blended paste should have a homogeneous appearance and a uniform consistency.
Cautions/Cautions
At room temperature, the material is valid for 2 years. Please refer to the outer box for the specific validity period. Expired products should not be used.
The material should be placed in a dark and dry place.
In the process of filling, repairing cavities with composite resin, or repairing cavities with dentin adhesive, when this product is used as a backing material, a layer of calcium hydroxide cement needs to be lined later.
After each use, please tighten the cap immediately so as not to affect the properties of the product.
This product is a special material for stomatology, non-professionals should not use it without permission, and special care should be taken not to let children touch it.
Use with caution in patients who are allergic to product ingredients.