Ultra-high bending strength and hardness
Comprehensive indications, especially for the long span bridge.
The excellent masking effect can be used for covering the metal color.
Bloomden white zirconia is unlike any other zirconia, it can exhibit a strength up to 1200MPa which can cover posteriors and anteriors for both crowns and bridges including implant restorations.
Bloomden zirconia is tension-free sintering without distortionand high accuracy of fit. High accuracy of fit, even for wide-span restorations
We provide exceptional color matching for VITA@'s full range of 16 shades, including BL2. Our quality is consistent across batches, and dental technicians in both Europe and the USA have confirmed our color accuracy.
| UT | HT-PLUS | ST | SHT | |
| ZrO2+Hf02+Y203ZrO2+Hf02+Y203 | ≥99% | ≥99% | ≥99% | ≥99% |
| Y203Y203 | 9%-10% | 4.5%-6.0% | 4.5%-6.0% | 7.0%-7.8% |
| AI203AI203 | <0.05% | <0.15% | <0.15% | <0.15% |
| Density beforesintering(g.cm-3)Density beforesintering(g.cm-3) | 3.20±0.05 | 3.15±0.05 | 3.15±0.05 | 3.15±0.05 |
| Density aftersintering(g.cm-3)Density aftersintering(g.cm-3) | 6.06±0.01 | 6.09±0.01 | 6.09±0.01 | 6.08±0.01 |
| CTE(25-500℃C)(K-1)CTE(25-500℃C)(K-1) | 10.5±0.5 | 10.5±0.5 | 10.5±0.5 | 10.5±0.5 |
| Flexural strengthafter sintering (MPa)Flexural strengthafter sintering (MPa) | >600 | >1350 | >1200 | >1000 |
| Aging surfacemonoclinic phasecontentAging surfacemonoclinic phasecontent | <15% | <15% | <15% | <15%< |
| Light transmittanceLight transmittance | <49% | <37% | 41%-43% | <46% |
| Chemical solubilityafter sintering(ug.cm-2)Chemical solubilityafter sintering(ug.cm-2) | <100 | <100 | <100 | <100 |
| CytotoxicityCytotoxicity | 0 Level | 0 Level | 0 Level | 0 Level |
| Radioactivity(Bq.g-1)Radioactivity(Bq.g-1) | <0.1 | <0.1 | <0.1 | <0.1 |
| Sinteringtemperature(℃℃)Sinteringtemperature(℃℃) | 1450 | 1530 | 1530 | 1530 |
| SystemsSystems | 98mm/95mm/92*75mm98mm/95mm/92*75mm | |||
| ThicknessThickness | 12m/14mm/16mm/18mm/20mm/22mm/25mm | |||
| ShadesShades | A1 A2 A3 A3.5 A4/B1 B2 B3 B4/C1 C2 C3 C4/D2 D3 D4 | |||